G6802V Polymethacrylate Viscosity Index Improver

Product introduction

Product performance

It is to be used for blending automatic transmission fluid.

This product has strong viscosity-increasing and finger-increasing capabilities, and also features low-temperature performance.

Effectively disperse impurities, such as soot and carbon deposits produced by the oxidation of oil during use, to extend the service life of the oil.

 

Project Quality standard Typical result Analytical method
Appearance Uniform and transparent Uniform and transparent Visual inspection
Kinematic viscosity(100℃)/m㎡/s 1800-2400 2120 GB/T265
Flash point (open)/℃ ≥160 180 GB/T3536
Moisture (mass fraction)/% Trace Trace GB/T260
Thickening ability/(m㎡/s) ≥13 15.1 GB/T265 note 1
Shear stability index of 30-cycle diesel nozzle ≤60 47.5 SH/T0103 note 2
Tilt point/℃ ≤-36 -45 GB/T3535 note 3
Conical roller KPL(60℃,20H)Shear stability index ≤90 79 NB/SH/T0845 note 2

 

Note 1: After adding 10%(by mass) of viscosity finger agent to HVIH5 base oil, the kinematic viscosity at 100℃ is the same as that of the base oil. The difference in kinematic viscosity at 100℃.

Note 2: After adding 7.5%(by mass fraction) of viscosity index to the HVIH5 base oil, measure its shear index.

Note 3: After adding 10%(by mass) of viscosity finger agent to the HVIH5 base oil, measure its pour point.



Just conducted a carbon black simulation test against Visoplex V12-709 with G6802V

ATF oil blending scheme ganghe G6802V Visoplex V12-709
Formosa Plastics 150N% 89.5 89.5
Finger adhesive% 3 3
Compound agent% 7.5 7.5
2%Carbon black, viscosity growth rate 13.08 13.76
ATF oil blending solution without compound agents: 89.5% Formosa 150n+3% dispersive sticky finger agent
2% carbon black, viscosity growth rate 53.43 53.30